Pengaruh Kecepatan Translasi dan Temperatur Pemanas Landasan Pelat Pada Friction Stir Welding Terhadap Kekuatan Bending Sambungan Las AA1100
Alumunium AA1100 is widely used in flat plate products such as heat exchanger fins and lightweight structural panels, yet it’s welding process still requires optimization. This study aims to determine the effect of tool traverse speed and backing plate preheating temperature on the bending strength of AA1100 joints produced by Friction Stir Welding (FSW). Experiments were conducted at three levels of each factor with three replications per combination: traverse speeds of 10 mm/min, 20 mm/min, 30 mm/min, and preheating temperatures of 200 °C, 250 °C, 300 °C. Results showed the travers speed, preheating temperature, and their interaction all had significant effects on bending strength (P-Value < 0,05). The optimal combination 30 mm/min traverse speed and 200 °C preheating yielded a bending strength of 238,95 Mpa. The regression model’s coefficient of determination was 97,16%, indicating an exellent fit. Thus, selecting the right FSW parameters can significanly enhancejoint quality.
Mohammad Irfan Yudhistira & Elka Faizal (2025). Pengaruh Kecepatan Translasi dan Temperatur Pemanas Landasan Pelat Pada Friction Stir Welding Terhadap Kekuatan Bending Sambungan Las AA1100. Jurnal Kendali Teknik dan Sains, 3(3). https://doi.org/10.59581/jkts-widyakarya.v3i3.5350
Mohammad Irfan Yudhistira; Elka Faizal, "Pengaruh Kecepatan Translasi dan Temperatur Pemanas Landasan Pelat Pada Friction Stir Welding Terhadap Kekuatan Bending Sambungan Las AA1100," Jurnal Kendali Teknik dan Sains, vol. 3, no. 3, 2025.
Mohammad Irfan Yudhistira; Elka Faizal. "Pengaruh Kecepatan Translasi dan Temperatur Pemanas Landasan Pelat Pada Friction Stir Welding Terhadap Kekuatan Bending Sambungan Las AA1100." Jurnal Kendali Teknik dan Sains, vol. 3, no. 3, 2025.
Mohammad Irfan Yudhistira; Elka Faizal. "Pengaruh Kecepatan Translasi dan Temperatur Pemanas Landasan Pelat Pada Friction Stir Welding Terhadap Kekuatan Bending Sambungan Las AA1100." Jurnal Kendali Teknik dan Sains 3, no. 3 (2025).
Mohammad Irfan Yudhistira & Elka Faizal (2025) 'Pengaruh Kecepatan Translasi dan Temperatur Pemanas Landasan Pelat Pada Friction Stir Welding Terhadap Kekuatan Bending Sambungan Las AA1100', Jurnal Kendali Teknik dan Sains, 3(3). doi: 10.59581/jkts-widyakarya.v3i3.5350.
Mohammad Irfan Yudhistira; Elka Faizal. Pengaruh Kecepatan Translasi dan Temperatur Pemanas Landasan Pelat Pada Friction Stir Welding Terhadap Kekuatan Bending Sambungan Las AA1100. Jurnal Kendali Teknik dan Sains. 2025;3(3).
Penggunaan Buzzer pada Modul GPS Teltonika FMB910 sebagai Indikator Kecepatan di PT Lacak Cipta Aktual
Aldi Bragi Muslim; Mohammad Fatkhurrokhman
Hubungan Minat Kejuruan dengan Kesiapan Memasuki Dunia Kerja Siswa Teknik Kendaraan Ringan Otomotif (Tkro) Smk Negeri 2 Sungai Penuh
M. Hifzon Fadhlika; Hasan Maksum; Irma Yulia Basri; Rifdarmon Rifdarmon
Analisa Penerapan Algoritma Keccak untuk Keamanan Permintaan API
Sofyan Noor Arief; Arief Prasetyo; Thariq Alfa Benriska
Identifikasi Penyakit Lambung Menggunakan Metode Case Based Reasoning Berbasis WEB
Surya Aulia Rahman. S; Ayu Prima Siska; Mardhotillah Mardhotillah
Studi Kasus Integrasi Current Transformer (CT) dan EOCR untuk Pengamanan Arus pada Panel Cooling Tower Pump di PT DongJin Indonesia
Muhammad Dicky Saputra; Mohammad Fatkurrokhman
Analisis Sentimen Publik TikTok dengan Pendekatan Lexicon-Based: Studi Kasus Timnas Indonesia di Piala Dunia 2026
Hamzah Nurrifqi Fakhri Fikrillah; Galih Pratama Herawan Putra; Fikri Chairul Ummam